The thickness of color steel tile is generally measured in millimeters (mm). Common thickness specifications cover multiple ranges from thinner to thicker, mainly including 0.2mm, 0.3mm, 0.4mm, 0.5mm, 0.6mm, 0.7mm, 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.5mm, etc.

Color steel tile comes in various thicknesses, depending on its intended use. Specifications are generally measured in millimeters (mm). Common thicknesses include: 0.2mm, 0.3mm, 0.4mm, 0.5mm, 0.6mm, 0.7mm, 0.8mm, 0.9mm, 1.0mm, 1.2mm, and 1.5mm.

In practical applications, four main thicknesses are commonly used: 0.3mm, 0.4mm, 0.5mm, and 0.6mm.
1. 0.3mm thick color steel tiles are thinner and suitable for temporary structures and warehouses with lower load-bearing requirements. This thickness is lightweight, easy to install, and relatively inexpensive.
2. 0.4mm thick sheets are relatively stronger and suitable for small factories and garages with certain load-bearing requirements, combining strength and economy.
3. 0.5mm thick sheets are suitable for large buildings and industrial facilities, such as large factories and stadiums, offering good load-bearing capacity and resistance to wind and rain erosion.
4. 0.6mm thick sheets are a thicker specification, used in applications requiring high load-bearing capacity and durability, such as roofs of high-rise buildings and exterior walls of important industrial facilities.

The core difference between hot-dip galvanized and cold-dip galvanized steel pipes stems from their drastically different production processes, which directly determine their performance, appearance, and applications.

1. Fundamentally Different Processes and Coatings:
Hot-dip galvanizing uses a "hot-dip coating" process, immersing the steel pipe in molten zinc at approximately 450°C. A metallurgical reaction occurs at high temperature, causing a strong bond between the zinc-iron alloy layer and the substrate. The coating is very thick (typically exceeding 60 micrometers) and has extremely strong adhesion.
Cold-dip galvanizing is actually "electro-galvanizing," where zinc ions adhere to the surface of the steel pipe at room temperature through electrolysis, forming a pure zinc coating. The coating is very thin (typically 5-20 micrometers), and the adhesion is mainly physical adsorption.

2. Significant Differences in Performance and Appearance:
Corrosion Resistance: Due to its thick and dense coating, hot-dip galvanized steel pipes have extremely strong corrosion resistance and can be used for decades in harsh outdoor environments. Cold galvanizing results in a thinner coating with weaker protection, primarily used in dry environments or for short-term rust prevention.
Mechanical Properties: Hot-dip galvanizing involves high temperatures, which slightly reduce the strength of the base material (low-carbon steel) but increase its toughness. Cold galvanizing, however, essentially does not alter the mechanical properties of the base material.
Appearance: Hot-dip galvanized surfaces are rougher, often with zinc bloom, and have a dark silver color. Cold-galvanized surfaces are smoother, more uniform, and brighter, resulting in a more aesthetically pleasing appearance.

3. Cost and Application Scenarios
Cost: Hot-dip galvanizing is a complex and energy-intensive process, leading to higher costs. Cold galvanizing is a simpler process with lower costs.
Applications: Based on these characteristics, hot-dip galvanized steel pipes are mainly used in heavily corrosive outdoor environments with long-term exposure, such as power transmission towers, highway guardrails, outdoor steel structures, and water pipelines. Cold-galvanized steel pipes are mostly used in indoor environments where aesthetics are important and the environment is dry, such as electrical wiring in home decoration, furniture frames, and small components.
When selecting, a comprehensive decision should be made based on the use environment, anti-corrosion life requirements and budget.